Composite  Powders  Series 

Powder Type

Chemistry

Morphology

Parameter

Particle Size

Properties and Applications

SY-321

Clad

Ni：80.0

Al：Bal

irregular

HRC=20

-140~325

l Dense coatings, resistant to oxidation and abrasion

l For oxidation resistant bond coats which will operate at temperatures below 650℃ (1200℉)

SY-322

Clad

Al：5.0

Ni：Bal

irregular

HRC=20

-140~325

l Coatings are dense and resistant to oxidation and abrasion

l Recommended for use as oxidation resistant bond coats which can be used up to 800℃ (1470℉) 

l Self-bonding material

l which exhibits an exothermic reaction during

l spraying resulting in a good bond.

SY-324

Clad

Al：5.0

Cr：17.0-19.0

Ni：Bal

irregular

HRC=20

-140~325

l Excellent corrosion and oxidation resistance

l Self bonding to most metallic  surfaces

l Good for general repair and build-up

SY-325

Clad

Cr：22.0

Al：11.0

Y：1.0

Ni：Bal

irregular

HRC=20-30

-140~325

l Coatings are usually used in aerospace applications and subsequently heat treated