Nano Series

Powder Type

Chemistry

Morphology

Parameter

Particle Size

Properties and Applications

SY-911

Spray Dried 

Sintered

Cr2O3≥99.0

Spheroidal

Black

2435℃

HRC=65~75

l -106~+38

l -50~+10

l Tough, dense and smooth, high hardness, excellent resistance to sliding and abrasive wear, erosion, cavitation and corrosion. 

l Coatings are insoluble in acids, alkalis and alcohol.

l Used as hard face wear, fibre abrasion, particle erosion, gas and liquid corrosion-resistant coatings.  

l Used on pump seal areas, rolls and wear rings

SY-921

Spray Dried 

Sintered

Al2O3≥99.0 Spheroidal

White

2038℃

HRC=60~70

l -106~+38

l -50~+10

l High hardness, excellent resistance to abrasive and sliding wear, erosion, cavitation and corrosion;

l high dielectric strength, service temperatures: 800℃

l Used as hard face wear, fibre abrasion;particle erosion and high temperature erosion resistant coatings.

SY-922

Spray Dried 

Sintered

TiO2:13.0

Al2O3:87.0

Spheroidal

Black/Grey

1890℃

HRC=60~70

l -90~+20

l Tough, dense and smooth, excellent resistance to abrasive wear, erosion, corrosion and fretting. 

l Resistant to high temperature up to 540℃ and most acids and caustics.

l High dielectric strength.

l Used as hard face wear;

l fibre abrasion and particle erosion-resistant coatings.

SY-931

Spray Dried 

Sintered

Y2O3:8.0

ZrO2:Bal.

Spheroidal

White

2480℃

HRC=35~45

l -90~+20

l Coatings exhibit good chemical and thermal stability.

l Tough and dense, excellent resistance to thermal shock and particle erosion at high temperature, good insulation. 

Applications:

l Used as thermal barrier coatings for turbine combustion liners and airfoils; 

l Particle erosion and hot gas corrosion protective coatings.