Investigation on antifouling coatings for ships and its evaluation of the effect of drag reduction

Time:2013-11-01 08:18:59  From:CNKI  Author:Zhou Hongfei

  ABSTRACT:
  When marine fouling organisms attach to a ship, they will accelerate corrosion of the vessel, increase the drag and fuel consumption. The traditional poison-release coating affect adversely the environment. Due to low surface energy, environment friendly,smooth surface and drag reduction performance, the fouling-release coating has the attention of scientists.
  In order to develop high drag reduction properties of the silicone fouling-release coatings, the research group designs the torque test device to study the relationship between structure of fouling-release coatings and its drag reduction properties.
  
  Self-polishing co- polymer(SPC),CDP and silicone fouling-release(FR) antifouling coatings are selected to evaluate the properties. 11 kinds of the silicone fouling-release coatings which are modified by powders are prepared and tested the properties.
  The results show that, compared with other two kinds of coatings, the surface of silicone fouling-release antifouling coating has low surface energy and high water contact angle. Besides, It provides a low-friction, ultra-smooth surface. The result of the single disk test shows the average drag reduction rate of FR with respect to S-7(SPC) is 13.50%,and the result of double cylinder test is 22.07%. The high drag reduction properties of FR is because of its high hydrophobicity and smooth surface. The results of testing panels in the sea show antifouling property of FR is worse than the other two kinds of coatings, but its foul-release property is better.
  The tests of 11 kinds of modified silicone coating show the powder of glass flake,nano-Ti02, smaller particle size of Al2O3(Al2O3-4) can improve the hardness of coatings. The powder of carbon nano-tube(CNT) and AI2O3-4 will increase water contact angle,enhance the hydrophobicity and reduce the surface energy of the coatings.
  The powder of iron oxide red, glass flake, Ti02 and CNT will reduce biological adhesion factor (Fi) of coatings,Then the testing panels in the sea confirm the results.The powder of CNT and AI2O3-4 can enhance the drag reduction properties of silicone coatings because of the strengthen hydrophobicity. With the thickness of coating increasing, the friction torque coefficient of 1-A9, 2-A4 coatings decrease. As a result of incrassation of elastomer in the coating, the strengthen flexibility of coating reduces friction between the coating and seawater,enhances the drag reduction properties.
  
  Key Words: Torque test device; Drag reduction; Silicone fouling-release coatings;Powder modification; Antifouling property
  
  
  
本站文章未经允许不得转载;如欲转载请注明出处,北京桑尧科技开发有限公司网址:http://en.sunspraying.com/
 

Support
返回首页
Home page
发表评论 共有条评论
用户名: 密码:
验证码: 匿名发表
Information
TiO2 used for plasma spraying rotatable targets
TiO2 used for plasma
Company Profile
Company Profile
The growth of Beijing Sunspraying New Material Co., Ltd.
The growth of Beijin
Article
    无相关信息
Update
Hot