A new high temperature resistant glass ceramic coating for gas turbine engine components
SOMESWAR DATTA, SUMANA DAS
Bull.Mater.Sci.
Abstract
A new high temperature and abrasion resistant glass ceramic coating system (based on MgO Al2O3 TiO2 and ZnO Al2O3 SiO2 based glass systems) for gas turbine engine components has been developed. Thermal shock resistance, adherence at 90 -bend test and static oxidation resistance at the required working temperature (1000 C) for continuous service and abrasion resistance are evaluated using suitable standard methods. The coating materials and the resultant coatings are characterized using differential thermal analy- sis, differential thermogravimetric analysis, X-ray diffraction analysis, optical microscopy and scanning elec- tron microscopy. The properties evaluated clearly showed the suitability of these coatings for protection of different hot zone components in different types of engines. XRD analysis of the coating materials and the resultant coatings showed presence of a number of microcrystalline phases. SEM micrographs indicate strong chemical bonding at the metal ceramic interface. Optical micrographs showed smooth glossy impervious defect free surface finish.
keywords:Coatings; Hot corrosion; Abrasion; Glass ceramic; vitreous enameling; high temperature resistance.
本站文章未经允许不得转载；如欲转载请注明出处，北京桑尧科技开发有限公司网址：http://www.sunspraying.com/
|