Relationship between microstructure of plasma-sprayed 8YZ coatings and thermal fatigue life of thermal barrier coatings
K. YASUDA, S. SUENAGA, H. INAGAKI
JOURNAL OF MATERIALS SCIENCE
abstract:Microstructure of plasma-sprayed yttria-stabilized zirconia coatings (8YZ) was characterized by the measurement of surface roughness, hardness, and pore size distribution and was correlated with thermal fatigue life. It was conrmed that the coatings which had greater roughness tended to show both lower hardness and higher porosity. Furthermore, such coatings were found to have a longer thermal fatigue life. We propose that measurement of the roughness of 8YZ coatings is useful as a non-destructive evaluation method for predicting thermal fatigue life.
keywords:TBCs; thermal fatigue; non-destructive evaluation