A steady-state Bi-substrate technique for measurement of the thermal conductivity of ceramic coatings
J.C. Tan, S.A. Tsipas, I.O. Golosnoy, J.A. Curran
Surface & Coatings Technology
abstract:This paper presents a steady-state, bi-substrate technique for measurement of the through-thickness thermal conductivity of ceramic coatings, with a range of specimen thickness and porosity content. The technique is based on establishing unidirectional steady-state heat flow through the sample, sandwiched between a pair of (metallic) substrates with known thermal properties. Comparison between the heat fluxes passing through the two substrates allows a check to be made about the accuracy of the assumption of unidirectional heat flow. The interfacial conductances must be known and these can be estimated by testing samples of different thickness. Measured conductivities are likely to be more accurate if the interfacial conductance is relatively high. This is assisted by the introduction of a thin interfacial layer of a viscous, thermally conductive compound, or thermal pads of some sort, and by maintaining a suitable pressure across the setup. However, if such compounds (pastes) are used, then care must be taken to ensure that it does not enter the specimen via surface-connected pores, since this could significantly affect the measured conductivity. The reliability of the technique has been confirmed by testing fused silica samples of known thermal conductivity. It has also been applied to sprayed zirconia and plasma electrolytic oxide (PEO) alumina coatings. The values obtained were 1.05 0.10W m1 K1 and 1.63 0.35W m1 K1, respectively.
keywords:Thermal conductivity; Thermal barrier coating; Interfacial thermal conductance; Ceramic coating; Plasma sprayed zirconia; Plasma electrolytic oxide coating
本站文章未经允许不得转载；如欲转载请注明出处，北京桑尧科技开发有限公司网址：http://www.sunspraying.com/
|