Effect of AL_3Ti diffusion aluminide coating on tensile properties of a near α-Ti alloy
Parlikar, C. ；Alam, M.Z. ；Das, D.K.
Materials Science & Engineering. A, Structural Materials: Properties, Misrostructure and Processing
The tensile properties of a near α Ti-alloy have been evaluated in both uncoated and diffusion aluminide (Al_3Ti) coated conditions at room temperature (RT) and 600°C. The effect of coating thickness on the tensile properties has been examined. The YS and UTS of the alloy at RT reduced marginally because of the presence of the coating, with the extent of reduction increasing with the increase of coating thickness. Such a trend in alloy strength was also observed at 600°C. The RT ductility of the alloy remained nearly unaffected by the presence of the coating. However, an increase in ductility was observed in the coated alloy at 600°C. The above effect of Al_3Ti coating on tensile properties of the present near α Ti-alloy has been explained in terms of the influence of the through-thickness cracking in the coating during tensile testing.
keywords: Al_3Ti coating Near α titanium alloy Oxidation Tensile properties
参考文献 略
本站文章未经允许不得转载；如欲转载请注明出处，北京桑尧科技开发有限公司网址：http://www.sunspraying.com/
|