A study on gradient thermal barrier coatings by EB-PVD in a cyclic high-temperature hot-corrosion environment
HONGBO GUO, HUIBIN XU, SHENGKAI GONG
JOURNAL OF MATERIALS SCIENCE
Abstract
Gradient thermal barrier coatings (GTBCs) have been produced by electron beam physical vapor deposition (EB-PVD). Their performance was evaluated by isothermal oxidation and cyclic high-temperature hot-corrosion tests. It is found that the GTBCs exhibited better resistance to high-temperature oxidation and cyclic high-temperature hot-corrosion (HTHC) than traditional two-layered TBCs. A dense Al2O3 layer on the bond coat of GTBCs can effectively prohibit inward diffusion of oxidants such as O and S and outward diffusion of Al and Cr. On the other hand, an inlaid interface, the formation of which resulted from the oxidation of Al diffusion into the gaps between the columns of bond coat during the fabrication of the GTBCs, contributes to reinforce the adherence of the Al2O3 layer to the bond coat. During uxing of the Al2O3 layer, S and O diffused into the bond coat. Cracks developed in the surface layer of bond coat by the combined effect of suldation of the bond coat and thermal cycling, and nally led to failure of the GTBC.
keywords:EB-PVD; bond coat; isothermal oxidation; outward; barrier coatings; GTBCs; hot-corrosion; better resistance
本站文章未经允许不得转载；如欲转载请注明出处，北京桑尧科技开发有限公司网址：http://www.sunspraying.com/
|