Microstructure and Tribological Properties of Plasma-sprayed Nanostructured Sulfide Coating

Time:2012-07-03 09:58:47  From:JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY  Author:Yang XU, Yaohui GUAN, Zhongyu

Microstructure and Tribological Properties of Plasma-sprayed Nanostructured Sulfide Coating

Yang XU, Yaohui GUAN, Zhongyu ZHENG
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY

abstract:The friction and wear properties of plasma-sprayed nanostructured FeS coating were investigated on an MHK- 500 friction and wear tester under both oil lubrication and dry friction condition. The microstructure, worn surface morphology and phase composition of the coating were characterized by scanning electron microscopy (SEM) and X-ray diraction (XRD). It was found that the coating was mainly composed of FeS, a small quantity of Fe1 S and oxide were also found. The coating was formed by small particles of 50 100 nm x in size. The thickness of the coating is approximately 150 m. The friction-reduction and wear-resistance properties of plasma-sprayed nanostructured FeS coating were superior to that of GCr15 steel substrate. Especially under oil lubrication condition, the friction coecient of nanostructured FeS coating was 50% of that of GCr15 steel, the wear scar widths of the coating were also reduced to nearly 50% of that of GCr15 steel under high load. The failure of the coating was mainly attributed to plastic deformation under both oil lubrication and dry friction condition.

keywords:Plasma spray; Sulfide; Friction and wear; Nanostructured