Nanostructured TiC/a-C coatings for low friction and wear resistant applications

Time:2020-08-16 10:03:17  From:  Author:

 The influence of the volume fraction and size distribution of nanocrystalline TiC (nc- TiC) on the coating properties has been examined. Closed-field unbalanced and balanced magnetron sputtering was used to deposit nanocrystalline TiC (nc-TiC)/amorphous carbon (a-C) nanocomposite coatings with hydrogenated or hydrogen-free a-C matrix, respectively. The contents of Ti and C in the coatings have been varied over the full range of interest (7–45 at.% Ti) by changing the flow rate of acetylene gas or the locations of substrates relative to the center of C/TiC targets. Different levels of bias and deposition pressure were used to control the nanostructure. The nanocomposite coatings exhibit hardness of 5–35 GPa, hardness/E-modulus ratio up to 0.15, wear rate of 4.8_10_17 m3/N m lap, friction coefficient of 0.04 under dry sliding and strong self-lubrication effects. The nanostructure and elemental distribution in the coatings have been characterized with cross-sectional and planar high-resolution transmission electron microscopy (HRTEM) and energy-filtered TEM. The influence of the volume fraction and size distribution of nc-TiC on the coating properties has been examined.

7.6.3.jpg


本文由桑尧热喷涂网收集整理。本站文章未经允许不得转载;如欲转载请注明出处,北京桑尧科技开发有限公司网址:http://www.sunspraying.com/ 

Support
返回首页
Home page
发表评论 共有条评论
用户名: 密码:
验证码: 匿名发表
Information
Article
    无相关信息
Update
Hot