Life time of new SYSZ thermal barrier coatings produced by plasma spraying method under thermal shock test and high temperature treatment

Time:2013-12-22 08:00:12  From:Ceramics International  Author:Mohammad Reza Loghman-Estarki,

Abstract
Nanostructured scandia (4.6 mol%), yttria (0.4 mol%) doped zirconia (5SYSZ) and 7 wt% yttria stabilized zirconia (7YSZ) thermal barrier coatings (TBCs) were produced by plasma spraying on nickel-based superalloy substrates with NiCrAlY as the bond coat. The thermal shock behavior of the two as-sprayed TBCs at 1000 °C was investigated. The results indicated that the thermal cycling lifetime of 7YSZ TBCs was longer than the 5SYSZ TBCs due to the lower thermal mismatch stress between the ceramic layer and the metallic layer at high temperature. However, the nanostructured 5SYSZ coating had higher thermal stability than 7YSZ TBC.

Keywords
C. Thermal shock resistance; Atmospheric plasma spraying; Durability of TBCs under thermal cycling; Nanostructured thermal barrier coatings

 

本站文章未经允许不得转载;如欲转载请注明出处,北京桑尧科技开发有限公司网址:http://en.sunspraying.com/
 

Support
返回首页
Home page
发表评论 共有条评论
用户名: 密码:
验证码: 匿名发表
Information
Article
    无相关信息
Update
Hot