Spraying TiN by a Combined Laser and Low-Pressure Plasma Spray System

Time:2012-06-29 09:20:32  From:Journal of Thermal Spray Technology   Author:A. Ohmori, S. Hirano, and K, K

Spraying TiN by a Combined Laser and Low-Pressure Plasma Spray System
A. Ohmori, S. Hirano, and K, Kamada

The formation of a TiN-Ti composite coating by thermal spraying of titanium powder with laser processing of the subsequent coating in a low-pressure N2 atmosphere was examined. A low-pressure plasma spray system was used in combination with a CO2 laser. First, the coating was plasma sprayed onto a mild steel substrate using a N2 plasma jet and titanium powder in a controlled low-pressure Nz atmosphere. The coating was then irradiated with a CO2 laser beam in a N2 atmosphere, and the coating was heated with a N2 plasma jet, The amount of TiN formed in the coating was characterized by X-ray diffraction analysis. The influence of plasma spraying conditions such as plasma power, flow of plasma operating gases, chamber pressure, and laser irradiating conditions on the formation of TiN was investigated. The effect of TiN formation in the titanium coating on Vickers hardness of the coatings was examined. It was evident that coating hardness increased with an increase in TiN content in the coating and that a TiN-Ti
composite coating with a hardness of more than 1200 HV can be obtained with the use of laser irradiation processing.

 


本站文章未经允许不得转载;如欲转载请注明出处,北京桑尧科技开发有限公司网址:http://www.sunspraying.com/
 

Support
返回首页
Home page
发表评论 共有条评论
用户名: 密码:
验证码: 匿名发表
Information
Article
    无相关信息
Update
Hot